Electrochemical studies on chalcocite-heazlewoodite system
Public Deposited- Creator
- Contributors
- Abstract
- Dissolution, rest potential, cyclic voltammetry and contact angle studies have been conducted on the components of INCO matte, chalcocite (Cu4$ sb{2}$S) and heazlewoodite (Ni$ sb{3}$S$ sb{2}$), in water and collector solutions. Dissolution of Ni from heazlewoodite was observed at pH .25 V. A reaction for MBT on chalcocite at $-$0.06 V, not reported previously, was proposed. Contact angle measurements were performed with chalcocite and heazlewoodite in the presence of 2 $ times$ 10$ sp{-3}$ M NaEX over a range of potential and pH values. A significant difference in contact angle between chalcocite and heazlewoodite was observed. There was general agreement between cyclic voltammograms and contact angle measurements: For example, the contact angle on Cu$ sb{2}$S in the presence of NaEX increased significantly at the potential range corresponding to passivation. No bubble contact was observed in the presence of 2 $ times$ 10$ sp{-3}$ M MBT.
English
- Last modified
- 2022-03-23
- Subject
- Publisher
- Language
- Identifier
- Rights
- All items in eScholarship@McGill are protected by copyright with all rights reserved unless otherwise indicated.
- Institution
- McGill University
- Department
- Degree
- Type
- Date
Relations
- In Collection: